| Product Name | Alloy Steel Pipe |
| Material | 30CrMnSiA |
| Outer Diameter(round) | 88.9mm |
| Certification | ISO DCDMA |
| Payment Terms | T/T, L/C |
| Technique | Hot Rolled |
| Standard | AISI, ASTM, DIN, JIS, GB |
30CrMnSi has high strength and toughness, high hardenability, medium cold deformation plasticity, good machinability, tendency to temper brittleness, and poor transverse impact toughness. The weldability is good, but when the thickness is greater than 3mm, it should be preheated before welding, and it needs to be heat treated in time after welding. Generally used after conditioning. In order to meet different needs, this steel can be tempered at low temperature or high temperature after quenching. Used to manufacture important parts working under high-speed and vibration loads, such as grinding wheel shafts, gears, sprockets, clutches, bushings, bolts, nuts, etc.; also used to manufacture wear-resistant, low-temperature parts and withstand alternating loads Welded components, such as high-pressure blower blades, valve plates, and non-corrosive pipes, etc.
30CrMnSi alloy steel plates Chemical composition (%)
Grade | C | Si | Mn | Cr |
30CrMnSi | 0.27-0.34 | 0.90-1.20 | 0.80-1.10 | 0.80-1.10 |
Mechanical Properties(In Quenched & Tempered State)
Tensile | Yield strength | Elongation | Reduction in | Impact | Hardness |
≥1080 | ≥ 835 | ≥ 10 | ≥ 45 | ≥ 39 | ≤229HBS |
30CrMnSi alloy steel plates are used to manufacture all kinds of important parts of high load and high speed, such as gear, shaft, clutch, sprocket, wheel shaft, shaft sleeve, bolt, nut and so on. 30CrMnSi steel is also used to make parts with wear resistance and not too high working temperature features, the variable load welded components, such as the blades of high pressure blower, valve plate and so on.
| 30CrMnSi alloy steel plates Chemical composition (%) | ||||
| Grade | C | Si | Mn | Cr |
| 30CrMnSi | 0.27-0.34 | 0.90-1.20 | 0.80-1.10 | 0.80-1.10 |
| Mechanical Properties(In Quenched & Tempered State) | |||||
| Tensile strength (MPA) | Yield strength (MPA) | Elongation (δ5/%) | Reduction in Area (ψ/%) | Impact (J) | Hardness |
| ≥1080 | ≥ 835 | ≥ 10 | ≥ 45 | ≥ 39 | ≤229HBS (not heat treatment) |
*Top 20 companies in steel industry trade volume.
*Customized processing steel one-stop purchase.
*Exports of steel exceeded tens of billions for 5 consecutive years.
**We have a complete set of testing equipment, such as ut & ET, hydraulic testing equipment, spectrometer, scanning electron microscope, etc, and have passed SGS TUV
Our Quality Assurance Policy has established guidelines for providing products and services that exceed customer expectations. certified company.